Direct production of hard magnetic ribbons with enhanced magnetic properties by controlling cooling rate of melt
Direct production of hard magnetic ribbons with enhanced magnetic properties by controlling cooling rate of melt
 
الموضوع : physics 
لغة الوثيقة : الانجليزية 
المستخلص : We produced a high-quality hard magnetic Fe81Co2Nb1Nd10B6 alloy by melt spinning without additional treatment. The as-spun ribbons produced at a wheel speed of similar to 25 m/s had the best hard magnetic properties: a remanence B-r, coercive force H-c, and maximum energy product (BH) (max) of 0.97 T, 676 kA/m, and 140 kJ/m(3), respectively. The Nd2Fe14B/alpha-Fe nanocomposite phases had grain sizes of similar to 10-30 nm. We investigated how the magnetic properties changed with wheel speed, finding that they depended on the as-spun structure and magnetic structure, which changed upon over-and under-quenching from the melt 
ردمد : 0021-8979 
اسم الدورية : JOURNAL OF APPLIED PHYSICS 
المجلد : 117 
العدد : 12 
سنة النشر : 1435 هـ
2015 م 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Monday, August 21, 2017 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
W.F ZhouZhou, W.F باحث رئيسيدكتوراه 
C.T ChangChang, C.T باحث مشاركدكتوراه 
A Inoue,Inoue,, A باحث مشاركدكتوراه 
X.M WangWang, X.M باحث مشاركدكتوراه 
F.S LiLi, F.S باحث مشاركدكتوراهfsli@zzu.edu.cn
J HuoHuo, J باحث مشاركدكتوراه 

الملفات

اسم الملفالنوعالوصف
 42719.pdf pdf 

الرجوع إلى صفحة الأبحاث