تفاصيل الوثيقة نوع الوثيقة : مقال في مجلة دورية  عنوان الوثيقة : Microwave Dielectric Properties of Lead Molybdenum Phosphate Glasses Microwave Dielectric Properties of Lead Molybdenum Phosphate Glasses   الموضوع : Microwave Dielectric Properties of Lead Molybdenum Phosphate Glasses  لغة الوثيقة : الانجليزية  المستخلص : Seven samples of lead molybdenum phosphate glasses are prepared due to mol % composition PbDx MoO3 (80 – x) P2O3(20) over the compositional ranges from x = 0 to 60. The microwave behavior of this kind of glasses is investigated in term of the microwave dielectric properties measurements at low temperature due to lead addition. The full computerized cavity perturbation technique working in microwave frequency ranges 615 MHz, 1412 MHz, 2214 MHz, 3017 MHz, and 3820 MHz are used for these measurements. The real ' and the imaginary '' parts of the complex permittivity are measured at room temperature and the frequency-dependent electrical conductivity  is calculated using the complex permittivity imaginary part ''. The frequency exponent n and the activation energy EA are determined using the calculated electrical conductivity . Microwave absorption is observed on the sample consisted of molybdenum and phosphate rather than the other samples with lead addition.  ردمد : 0  اسم الدورية : J. Egypt. J. Solids  المجلد : 29  العدد : 1  سنة النشر : 1427 هـ 2006 م  عدد الصفحات : 6  نوع المقالة : مقالة علمية  تاريخ الاضافة على الموقع : Thursday, July 2, 2009  الباحثون اسم الباحث (عربي) اسم الباحث (انجليزي) نوع الباحث المرتبة العلمية البريد الالكتروني ثريا Thoria باحث دكتوراه   الرجوع إلى صفحة الأبحاث